NSUF 20-2972: Investigating the effect of irradiation on hydride formation and morphology in zirconium alloys
This work will investigate the morphology and interconnectivity of hydrides in an irradiated zirconium alloy. By comparing the hydride formation in non-irradiated and proton-irradiated Zircaloy-4 samples we will develop a better understanding of the behaviour of hydrides. Hydrides in zirconium alloys are of key interest for both Canadian and American civil nuclear reactors. This is due to their significant effect on reducing the fracture toughness of key fuel assembly components, such as fuel cladding. Even small amounts of H (~10s of ppm/weight) can significantly reduce the material fracture toughness and make it susceptible to a sub-critical crack growth mechanism known as Delayed Hydride Cracking (DHC). Hydrides may also significantly affect the performance of cladding during storage of spent fuel simply through embrittlement. Preventing hydrogen embrittlement/DHC failures requires an accurate and detailed understanding of the behavior of small quantities of hydrogen in zirconium.
Prior to this proposed experiment, notched Zircaloy samples containing 100 wt.ppm hydrogen will be proton-irradiated at the Reactor Materials Testing Laboratory (RMTL) at Queen’s University. The samples will be irradiated at 5MeV to ~1dpa at 350°C in order to have significant irradiation defects in the metal before hydride formation at a notch tip. Following the irradiation, these notched samples will be heated up to 350°C to dissolve the pre-existing hydride; then a load is applied and the sample is cooled down at a rate of 1°C/minute. This ratcheting thermal cycle will be repeated multiple times to ensure enough hydrides precipitate at the notch tip. We have already seen that at the length scales viewable by TEM that the hydrides generated in irradiated and unirradiated materials have different morphology. Here we will study the hydride morphology at a longer length scale using the FEI Helios plasma focused ion beam (PFIB) at Idaho National Laboratory. Through serial sectioning and the reconstruction to produce 3D-EBSD data we will gain an understanding of the interaction between the matrix and hydrides and also the interaction between hydrides; the key question to be explored is the hydride connectivity which then influences crack-path. Information obtained in traditional 2D-EBSD analysis is not sufficient as one only obtains information from a single surface but hydrides are complex 3D structures. In conjunction with the proposed experiment we will test identical samples to failure and study the fracture surfaces using the materials characterisation suite at RMTL.
Demonstrating the difference in hydride formation around a notch tip between non-irradiated and irradiated samples is key in developing more accurate models to understand the impact of hydrides on failure. The data collected as part of the work has the potential to significantly impact the global nuclear industry as hydride embrittlement is a key issue currently limiting the efficiency of nuclear energy.
Additional Info
| Field | Value |
|---|---|
| Abstract | This work will investigate the morphology and interconnectivity of hydrides in an irradiated zirconium alloy. By comparing the hydride formation in non-irradiated and proton-irradiated Zircaloy-4 samples we will develop a better understanding of the behaviour of hydrides. Hydrides in zirconium alloys are of key interest for both Canadian and American civil nuclear reactors. This is due to their significant effect on reducing the fracture toughness of key fuel assembly components, such as fuel cladding. Even small amounts of H (~10s of ppm/weight) can significantly reduce the material fracture toughness and make it susceptible to a sub-critical crack growth mechanism known as Delayed Hydride Cracking (DHC). Hydrides may also significantly affect the performance of cladding during storage of spent fuel simply through embrittlement. Preventing hydrogen embrittlement/DHC failures requires an accurate and detailed understanding of the behavior of small quantities of hydrogen in zirconium. Prior to this proposed experiment, notched Zircaloy samples containing 100 wt.ppm hydrogen will be proton-irradiated at the Reactor Materials Testing Laboratory (RMTL) at Queen’s University. The samples will be irradiated at 5MeV to ~1dpa at 350°C in order to have significant irradiation defects in the metal before hydride formation at a notch tip. Following the irradiation, these notched samples will be heated up to 350°C to dissolve the pre-existing hydride; then a load is applied and the sample is cooled down at a rate of 1°C/minute. This ratcheting thermal cycle will be repeated multiple times to ensure enough hydrides precipitate at the notch tip. We have already seen that at the length scales viewable by TEM that the hydrides generated in irradiated and unirradiated materials have different morphology. Here we will study the hydride morphology at a longer length scale using the FEI Helios plasma focused ion beam (PFIB) at Idaho National Laboratory. Through serial sectioning and the reconstruction to produce 3D-EBSD data we will gain an understanding of the interaction between the matrix and hydrides and also the interaction between hydrides; the key question to be explored is the hydride connectivity which then influences crack-path. Information obtained in traditional 2D-EBSD analysis is not sufficient as one only obtains information from a single surface but hydrides are complex 3D structures. In conjunction with the proposed experiment we will test identical samples to failure and study the fracture surfaces using the materials characterisation suite at RMTL. Demonstrating the difference in hydride formation around a notch tip between non-irradiated and irradiated samples is key in developing more accurate models to understand the impact of hydrides on failure. The data collected as part of the work has the potential to significantly impact the global nuclear industry as hydride embrittlement is a key issue currently limiting the efficiency of nuclear energy. |
| Award Announced Date | 2020-02-05T14:11:36.05 |
| Awarded Institution | None |
| Facility | None |
| Facility Tech Lead | Alina Zackrone |
| Irradiation Facility | None |
| PI | Mark Daymond |
| PI Email | [email protected] |
| Project Type | RTE |
| RTE Number | 2972 |